(1) 20CrMnMo steel small gear by using nitrogen methanol atmosphere at 860 ℃ carbonitriding, ammonia accounted for about 3%, the total volume of furnace gas carbon potential 0.8% more appropriate. The nitrogen methanol atmosphere of Carbonitriding with energy saving, environmental protection, safety, low cost and fast penetration advantages.
(2) the small gear carbonitriding after re heating quenching, the layer has higher strength and hardness, and can make the core hardness meet the technical requirements, the plasticity and toughness. Temperature and quenching temperature carbonitriding for use low, control of quenching cooling rate plus, workpiece distortion decreases.
-
1
Brazing of aluminum frameProduct：Brazing of aluminum frame
Similar Articles
- Welding method of cast iron parts
- Reduce large structure welding deformation technological countermeasures
- Welding history
- Laser spot welding technology is analysed
- The way to prevent the welding spatter
- Titanium alloy laser repair welding technology
- The welding of titanium alloy and testing
- The point of use of stainless steel electrode should notice
- The role of argon gas in welding
- The impact of high temperature alloy welding
Latest News
- Welding method of cast iron parts
- Reduce large structure welding deformation technological countermeasures
- Welding history
- Laser spot welding technology is analysed
- The way to prevent the welding spatter
- Titanium alloy laser repair welding technology
- The welding of titanium alloy and testing
- The point of use of stainless steel electrode should notice
- Welding transverse crack reason mainly has the following several aspects
- The role of argon gas in welding
History
- Shenzhen Su's heat treatment and compound modification processing of Zr and Ti on the microstructure of ZA27 alloy obtained three conclusions
- Effect of Annealing on non synchronous rolling high purity aluminum foil structure
- Shenzhen Su's heat treatment distortion on the slender shaft nitriding control improvement measures and effects
- Pre-hardened mold material
- Use of welding and cutting machine operation security technology
- Welding transverse crack reason mainly has the following several aspects
Su's heat treatment (Shenzhen) Co., Ltd. Guangdong ICP No. 14020634
service hotline: 0755-27291255
Fax: support for 0755-27293730
E-MAIL:sushirechuli@163.com
Company address: Shenzhen, Baisha bridge Second Industrial Zone No. 14