Shenzhen Su's heat treatment processing that Cr20 heat treatment process
1: Cr20 cast iron thermal test index of the processing parameters in orthogonal test is the most important to the hardness, tempering temperature, then holding time for quenching, RE heat preservation time for quenching temperature and tempering.
2: at the same time, heat treatment process after casting can keep the impact toughness is basically unchanged effectively enhance the Cr20 hardness of the iron, experiments the hardness reached more than 57.5HRC. Optimal scheme of heat 960 ℃× 2.5h air quenched +450 ℃× 3.5H tempering treatment can obtain the highest hardness of 61.6HRC, the impact toughness of 2.31J/ cm 2, composition microstructure consists of hard shaped eutectic carbides and martensite matrix.
Shenzhen Su's heat treatment processing factory has been chasing the processing technology of heat treatment, welcome to the industry colleagues to come to discuss, developed a heat treatment process of optimal heat treatment, will carry forward the cause of.
-
1
Brazing of aluminum frameProduct：Brazing of aluminum frame
Similar Articles
- Welding method of cast iron parts
- Reduce large structure welding deformation technological countermeasures
- Welding history
- Laser spot welding technology is analysed
- The way to prevent the welding spatter
- Titanium alloy laser repair welding technology
- The welding of titanium alloy and testing
- The point of use of stainless steel electrode should notice
- The role of argon gas in welding
- The impact of high temperature alloy welding
Latest News
- Welding method of cast iron parts
- Reduce large structure welding deformation technological countermeasures
- Welding history
- Laser spot welding technology is analysed
- The way to prevent the welding spatter
- Titanium alloy laser repair welding technology
- The welding of titanium alloy and testing
- The point of use of stainless steel electrode should notice
- Welding transverse crack reason mainly has the following several aspects
- The role of argon gas in welding
History
- Shenzhen Su's heat treatment on Microstructure and mechanical ring back after cryogenic treatment of high speed steel performance summary
- Shenzhen Su's heat treatment is discussed effect of intercritical quenching on Microstructure and properties of steel 10Ni5CrMo results
- Shenzhen Su's heat treatment heat treatment process automation management
- Shenzhen Su's heat treatment factory of precipitates of austenitic stainless steel and resistance to corrosion and wear resistance of the three results of
- The central government budget this year invest 170000000000 yuan to promote energy-saving emission reduction
- 6061 water-cooled panel vacuum brazing
- Shenzhen Su's heat treatment of 40Cr steel gear surface punctate stripping failure analysis, draws the conclusion and suggestions to share with you:
- Casting mold vacuum hardening
- 303 stainless steel vacuum brazing, vacuum brazing of stainless steel
- DC53 heat treatment
Su's heat treatment (Shenzhen) Co., Ltd. Guangdong ICP No. 14020634
service hotline: 0755-27291255
Fax: support for 0755-27293730
E-MAIL:sushirechuli@163.com
Company address: Shenzhen, Baisha bridge Second Industrial Zone No. 14